Scratch Resistance Testing of Phone Screen Protectors

Andrew Shore — Wed, 12 Nov 2025 17:42:04 +0000

Scratch Resistance Testing of Phone Screen Protectors

Prepared by

Stacey Pereira, Jocelyn Esparza, and Pierre Leroux

Understanding Scratch Resistance in Phone Screen Protectors

Protective coatings on phone screens play a critical role in scratch resistance, adhesion strength, and long-term durability. Over time, scratches, micro-cracks, and coating delamination can reduce optical clarity and reliability — especially in high-use environments. To evaluate how different screen protectors resist mechanical damage, instrumented scratch testing provides quantifiable insight into coating failure mechanisms, including adhesion, cohesion, and fracture behavior.

In this study, NANOVEA PB1000 Mechanical Tester is used to compare TPU vs. tempered-glass screen protectors under controlled progressive loading. Using precise acoustic emission detection, we identify critical failure loads and characterize how each material responds to increasing mechanical stress.

Why Scratch Resistance Testing Matters for Screen Protectors

Many users assume that thicker or harder protectors automatically perform better, but real durability depends on how the material behaves under progressive load, surface deformation, and localized stress. Instrumented scratch testing allows engineers to measure coating adhesion, cohesive strength, surface wear resistance, and the exact loads at which failures initiate or propagate.

By analyzing crack initiation points, delamination behavior, and failure modes, manufacturers can validate screen-protector performance for R&D, quality control, or comparative benchmarking. Nano- and micro-scratch testing offer repeatable, data-driven insight into real-world durability far beyond traditional hardness ratings.

ℹ️ Learn more about scratch and adhesion testing services for coatings and screen protectors.

Scratch Testing Objective:
Measuring Failure Loads in Screen Protectors

The objective of this study is to demonstrate how the NANOVEA PB1000 Mechanical Tester performs repeatable, standardized scratch resistance testing on both polymeric and glass screen protectors. By progressively increasing the applied load, the system detects critical loads for cohesive and adhesive failure, captures acoustic emission signals, and correlates these events with scratch depth, friction force, and surface deformation.

This methodology provides a complete mechanical profile of each protective coating, allowing manufacturers and R&D teams to evaluate material formulations, coating adhesion strength, surface durability, and optimal coating thickness for improved product performance. These scratch evaluations are part of NANOVEA’s broader suite of mechanical testing solutions used to characterize coatings, films, and substrates across R&D, quality control, and production environments.

NANOVEA PB1000 Large-Platform
Mechanical Tester

Scratch Test Parameters and Instrument Setup

The scratch resistance evaluation of TPU and tempered-glass screen protectors was conducted under controlled conditions to ensure repeatability and accurate failure-load detection. The following parameters define the progressive-load scratch testing setup used on the NANOVEA PB1000 Mechanical Tester.

LOAD TYPE	PROGRESSIVE
INITIAL LOAD	0.1 N
FINAL LOAD	12 N
SLIDING SPEED	3.025 mm/min
SLIDING DISTANCE	3 mm
INDENTER GEOMETRY	ROCKWELL (120° CONE)
INDENTER MATERIAL (TIP)	DIAMOND
INDENTER TIP RADIUS	50 µm
ATMOSPHERE	AIR
TEMPERATURE	24 °C (ROOM TEMP)

TABLE 1: Test parameters used for scratch testing

Screen protector sample mounted on the NANOVEA PB1000 Mechanical Tester during progressive-load scratch measurement.

Screen Protector Samples Used for Scratch Resistance Testing

Two commercially available screen protector materials were selected to compare differences in scratch resistance, failure behavior, and mechanical durability. Both samples were mounted securely on the NANOVEA PB1000 Mechanical Tester and evaluated under identical progressive-load conditions to ensure a consistent and unbiased comparison.

The TPU screen protector represents a flexible polymeric film with high elasticity but lower abrasion resistance, while the tempered-glass protector represents a rigid, brittle material designed for high hardness and enhanced impact protection. Testing both materials under the same load profile allows a clear assessment of how material composition, elasticity, and hardness influence scratch failure modes.

TPU Screen Protector

Tempered Glass

FIGURE 1: TPU and tempered-glass screen protectors prepared for scratch resistance testing.

Scratch Test Results: Failure Modes in TPU vs. Tempered Glass Screen Protectors

TYPE OF SCREEN PROTECTOR	CRITICAL LOAD #1 (N)	CRITICAL LOAD #2 (N)
TPU	n/a	2.004 ± 0.063
TEMPERED GLASS	3.608 ± 0.281	7.44 ± 0.995

TABLE 2: Summary of critical loads for each screen protector sample.

Because TPU and tempered-glass screen protectors have fundamentally different mechanical properties, each sample exhibited distinct failure modes and critical load thresholds during progressive-load scratch testing. Table 2 summarizes the measured critical loads for each material.

Critical Load #1 represents the first observable point of cohesive failure under optical microscopy, such as crack initiation or radial fracture.

Critical Load #2 corresponds to the first major event detected through acoustic emission (AE) monitoring, typically representing a larger structural failure or penetration event.

TPU Screen Protector — Flexible Polymer Behavior

The TPU screen protector exhibited only one significant critical event (Critical Load #2). This load corresponds to the point along the scratch track where the film began to lift, peel, or delaminate from the phone screen surface.

Once Critical Load #2 (≈2.00 N) was exceeded, the indenter penetrated sufficiently to cause a visible scratch directly on the phone screen for the remainder of the test. No separate Critical Load #1 event was detectable, consistent with the material’s high elasticity and lower cohesive strength.

Tempered Glass Screen Protector — Brittle Failure Behavior

The tempered-glass screen protector showed two distinct critical loads, characteristic of brittle materials:

Critical Load #1 (≈3.61 N): Radial fractures and crack initiation were observed under the microscope, indicating early cohesive failure of the glass layer.
Critical Load #2 (≈7.44 N): A large AE spike and a sharp increase in scratch depth indicated protector penetration at higher loads.

Although the AE magnitude was higher than TPU, no damage was transferred to the phone screen, demonstrating the tempered-glass protector’s ability to absorb and distribute load before catastrophic failure.

In both materials, Critical Load #2 corresponded to the moment when the indenter broke through the screen protector, confirming the protective limit of each sample.

TPU Screen Protector: Scratch Test Data and Failure Analysis

SCRATCH	CRITICAL LOAD #2 (N)
1	2.033
2	2.047
3	1.931
AVERAGE	2.003
STANDARD DEVIATION	0.052

TABLE 3: Critical loads measured during TPU screen protector scratch testing.

FIGURE 2: Friction force, normal load, acoustic emission (AE), and scratch depth vs. scratch length for the TPU screen protector. (B) Critical Load #2

FIGURE 3: Optical microscopy image of the TPU screen protector at Critical Load #2 (5× magnification; image width 0.8934 mm).

FIGURE 4: Full-length post-scratch image of the TPU screen protector showing the complete scratch track following progressive-load testing.

Tempered Glass Screen Protector: Critical Load Data and Fracture Behavior

SCRATCH	CRITICAL LOAD #1 (N)	CRITICAL LOAD #2 (N)
1	3.923	7.366
2	3.382	6.483
3	3.519	8.468
AVERAGE	3.653	6.925
STANDARD DEVIATION	0.383	0.624

TABLE 4: Critical loads measured during tempered-glass screen protector scratch testing.

ℹ️ For comparison with non-silicate polymer coatings, see our study on PTFE coating wear testing, which highlights failure behavior in low-friction polymer films under similar progressive-load conditions.

FIGURE 5: Friction force, normal load, acoustic emission (AE), and scratch depth vs. scratch length for the tempered-glass screen protector. (A) Critical Load #1 (B) Critical Load #2

FIGURE 6: Optical microscopy images showing the failure locations for Critical Load #1 (left) and Critical Load #2 (right) at 5× magnification (image width: 0.8934 mm).

FIGURE 7: Post-test optical microscopy image of the tempered-glass scratch track, highlighting fracture initiation (CL#1) and the final penetration zone (CL#2) following progressive-load testing.

Conclusion: Scratch Performance Comparison of TPU vs. Tempered Glass Screen Protectors

This study demonstrates how the NANOVEA PB1000 Mechanical Tester delivers controlled, repeatable, and highly sensitive scratch resistance measurements using progressive loading and acoustic emission (AE) detection. By precisely capturing both cohesive and adhesive failure events, the system enables a clear comparison of how TPU and tempered-glass screen protectors behave under increasing mechanical stress.

The experimental results confirm that tempered glass exhibits significantly higher critical loads than TPU, providing superior scratch resistance, delayed fracture initiation, and reliable protection against indenter penetration. TPU’s lower cohesive strength and earlier delamination highlight its limitations in high-stress environments.

After identifying failure loads, the resulting scratch tracks can also be analyzed using a non-contact 3D optical profilometer to measure groove depth, residual deformation, and post-scratch topography. This helps complete the mechanical profile of each material.

The NANOVEA Mechanical Tester is engineered for accurate and repeatable indentation, scratch, and wear testing, and supports ISO- and ASTM-compliant nano and micro modules. Its versatility makes it an ideal solution for evaluating the full mechanical profile of thin films, coatings, polymers, glasses, and substrates across R&D, production, and quality control.

Frequently Asked Questions
About Scratch Resistance Testing

What is scratch resistance testing?

Scratch resistance testing evaluates how a material or coating responds when a diamond stylus applies a progressively increasing load. The test identifies the critical loads where cohesive or adhesive failures occur, providing a quantifiable measure of durability, adhesion strength, and resistance to surface damage.

What’s the difference between cohesive and adhesive failure?

Cohesive failure occurs within the coating or material, such as cracking, tearing, or internal fracture.
Adhesive failure happens when the coating detaches from the substrate, indicating insufficient bonding strength.

The NANOVEA PB1000 detects both using synchronized acoustic emission monitoring, scratch depth tracking, and friction analysis.

Why use a mechanical tester instead of manual methods?

A mechanical tester like the NANOVEA PB1000 provides precise, repeatable, and standardized measurements, ensuring reliable data for R&D, production validation, and quality control. It also offers advanced features, such as acoustic emission detection and real-time depth monitoring, that manual methods cannot deliver.

Need Reliable Scratch Testing for Your Materials?

The post Scratch Resistance Testing of Phone Screen Protectors appeared first on NANOVEA: Advanced Profilometers, Tribometers, Nanoindenters, and Scratch Testers for Materials Testing.

Microparticles: Compression Strength and Micro Indentation

nanovea — Tue, 28 Jul 2020 18:13:50 +0000

MICROPARTICLES

COMPRESSION STRENGTH & MICRO INDENTATION
BY TESTING SALTS

Author:
Jorge Ramirez

Revised by:
Jocelyn Esparza

INTRODUCTION

Compression strength has become vital to quality control measurement in developing and improving new and existing microparticles and micro features (pillars and spheres) seen today. Microparticles have various shapes, sizes and can be developed from ceramics, glass, polymers, and metals. Uses include drug delivery, food flavor enhancement, concrete formulations among many others. Controlling the mechanical properties of microparticles or microfeatures are critical for their success and requires the ability to quantitatively characterize their mechanical integrity

IMPORTANCE OF DEPTH VERSUS LOAD COMPRESSION STRENGTH

Standard compressive measurement instruments are not capable of low loads and fail to provide adequate depth data for microparticles. By using Nano or Microindentation, the compression strength of nano or microparticles (soft or hard) can be accurately and precisely measured.

MEASUREMENT OBJECTIVE

In this application note we measure the compression strength of salt with the NANOVEA Mechanical Tester in micro indentation mode.

NANOVEA

CB500

TEST CONDITIONS

maximum force

30 N

loading rate

60 N/min

unloading rate

60 N/min

indenter type

Flat Punch

Steel | 1mm Diameter

Load vs depth curves

Results & Discussion

Height, failure force and strength for Particle 1 and Particle 2

Particle failure was determined to be the point where the initial slope of the force vs. depth curve began to noticeably decrease.This behavior shows the material has reached a yield point and is no longer able to resist the compressive forces being applied. Once the yield point is surpassed, the indentation depth begins to exponentially increase for the duration of the loading period. These behaviors can be seen in Load vs Depth Curves for both samples.

CONCLUSION

In conclusion, we have shown how the NANOVEA Mechanical Tester in micro indentation mode is a great tool for compression strength testing of microparticles. Although the particles tested are made of the same material, it is suspected that the different failure points measured in this study were likely due to pre-existent micro cracks in the particles and varying particle sizes. It should be noted that for brittle materials, acoustic emission sensors are available to measure the beginning of crack propagation during a test.

The NANOVEA Mechanical Tester offers depth displacement resolutions down to the sub nanometer level,
making it a great tool for the study of very fragile micro particles or features as well. For soft and fragile
materials, loads down to 0.1mN are possible with our nano indentation module

Got a similar application?

The post Microparticles: Compression Strength and Micro Indentation appeared first on NANOVEA: Advanced Profilometers, Tribometers, Nanoindenters, and Scratch Testers for Materials Testing.

Improve Mining Procedures With Microindendation

nanovea — Mon, 11 May 2020 16:08:36 +0000

MICROINDENTATION RESEARCH AND QUALITY CONTROL

Rock mechanics is the study of the mechanical behavior of rock masses and is applied in mining, drilling, reservoir production, and civil construction industries. Advanced instrumentation with precise measurement of mechanical properties allows for part and procedure improvement within these industries. Successful quality control procedures are ensured by understanding rock mechanics at the micro scale.

Microindentation is a crucial tool used for rock mechanics related studies. These techniques advance excavation techniques by providing further understanding of rock mass properties. Microindentation is used to improve drill heads which improve mining procedures. Microindentation has been used to study chalk and powder formation from minerals. Microindentation studies can include hardness, Young’s modulus, creep, stress-strain, fracture toughness, and compression with a single instrument.

MEASUREMENT OBJECTIVE

In this application the Nanovea mechanical tester measures the Vickers hardness (Hv), Young’s modulus, and fracture toughness of a mineral rock sample. The rock is made up of biotite, feldspar and quartz which form the standard granite composite. Each is tested separately.

RESULTS AND DISCUSSION

This section includes a summary table that compares the main numerical results for the different samples, followed by the full result listings, including each indentation performed, accompanied by micrographs of the indentation, when available. These full results present the measured values of Hardness and Young’s modulus as the penetration depth (Δd) with their averages and standard deviations. It should be considered that large variation in the results can occur in the case that the surface roughness is in the same size range as the indentation.

Summary table of main numerical results for Hardness and Fracture Toughness

CONCLUSION

The Nanovea mechanical tester demonstrates reproducibility and precise indentation results on the hard surface of mineral rock. Hardness and Young’s modulus of each material forming the granite was measured directly from depth versus load curves. The rough surface meant testing at higher loads that may have caused micro cracking. Micro cracking would explain some of the variations seen in measurements. Cracks were not perceivable through standard microscopy observation because of a rough sample surface. Therefore, it is not possible to calculate traditional fracture toughness numbers that requires cracks length measurements. Instead, we used the system to detect initiation of cracks through the dislocations in the depth versus load curves while increasing loads.

Fracture threshold loads were reported at loads where failures occurred. Unlike traditional fracture toughness tests that simply measure crack length, a load is obtained at which threshold fracture starts. Additionally, the controlled and closely monitored environment allows the measurement of hardness to use as a quantitative value for comparing a variety of samples.

NOW, LET'S TALK ABOUT YOUR APPLICATION

The post Improve Mining Procedures With Microindendation appeared first on NANOVEA: Advanced Profilometers, Tribometers, Nanoindenters, and Scratch Testers for Materials Testing.

3 Point Bend Test Using Microindentation

nanovea — Thu, 07 Mar 2013 19:34:04 +0000

In this application, the Nanovea Mechanical Tester, in Microindentation mode, is used to measure the flexural strength (using 3 Point Bend) of various sized rod samples (pasta) to show a range of data. 2 different diameters were chosen to demonstrate both elastic and brittle characteristics. Using a flat tip indenter to apply a point load, we determine stiffness (Young’s Modulus) and identify the critical loads at which the sample will fracture.

3 Point Bend Test Using Microindentation

The post 3 Point Bend Test Using Microindentation appeared first on NANOVEA: Advanced Profilometers, Tribometers, Nanoindenters, and Scratch Testers for Materials Testing.

Indentation | Fracture Toughness Application Notes - NANOVEA: Advanced Profilometers, Tribometers, Nanoindenters, and Scratch Testers for Materials Testing

Scratch Resistance Testing of Phone Screen Protectors

Scratch Resistance Testing of Phone Screen Protectors

Understanding Scratch Resistance in Phone Screen Protectors

Why Scratch Resistance Testing Matters for Screen Protectors

Scratch Testing Objective: Measuring Failure Loads in Screen Protectors

Scratch Test Parameters and Instrument Setup

Screen Protector Samples Used for Scratch Resistance Testing

Scratch Test Results: Failure Modes in TPU vs. Tempered Glass Screen Protectors

TPU Screen Protector — Flexible Polymer Behavior

Tempered Glass Screen Protector — Brittle Failure Behavior

TPU Screen Protector: Scratch Test Data and Failure Analysis

Tempered Glass Screen Protector: Critical Load Data and Fracture Behavior

Conclusion: Scratch Performance Comparison of TPU vs. Tempered Glass Screen Protectors

Frequently Asked Questions About Scratch Resistance Testing

What is scratch resistance testing?

What’s the difference between cohesive and adhesive failure?

Why use a mechanical tester instead of manual methods?

Need Reliable Scratch Testing for Your Materials?

Microparticles: Compression Strength and Micro Indentation

MICROPARTICLES

COMPRESSION STRENGTH & MICRO INDENTATION BY TESTING SALTS​

Author:Jorge Ramirez

Revised by:Jocelyn Esparza

INTRODUCTION

IMPORTANCE OF DEPTH VERSUS LOAD COMPRESSION STRENGTH

TEST CONDITIONS

maximum force

30 N

loading rate

60 N/min

unloading rate

60 N/min

indenter type

Flat Punch

Steel | 1mm Diameter

Load vs depth curves

Results & Discussion

CONCLUSION

Got a similar application?

Improve Mining Procedures With Microindendation

NOW, LET'S TALK ABOUT YOUR APPLICATION

3 Point Bend Test Using Microindentation

Scratch Testing Objective:
Measuring Failure Loads in Screen Protectors

Frequently Asked Questions
About Scratch Resistance Testing

COMPRESSION STRENGTH & MICRO INDENTATION
BY TESTING SALTS

Author:
Jorge Ramirez

Revised by:
Jocelyn Esparza