{"id":22101,"date":"2023-05-17T14:15:13","date_gmt":"2023-05-17T14:15:13","guid":{"rendered":"https:\/\/nanovea.com\/?p=22101"},"modified":"2025-05-22T19:07:17","modified_gmt":"2025-05-22T19:07:17","slug":"analisi-meccanica-dinamica-del-sughero-mediante-nanoindentazione","status":"publish","type":"post","link":"https:\/\/nanovea.com\/it\/analisi-meccanica-dinamica-del-sughero-mediante-nanoindentazione\/","title":{"rendered":"Analisi meccanica dinamica del sughero mediante nanoindentazione"},"content":{"rendered":"
\n\t\t\t\t\t\t
\n\t\t\t\t\t\t
\n\t\t\t\t\t
\n\t\t\t
\n\t\t\t\t\t\t
\n\t\t\t\t
\n\t\t\t\t\t

ANALISI MECCANICA DINAMICA<\/h1>\t\t\t\t<\/div>\n\t\t\t\t<\/div>\n\t\t\t\t
\n\t\t\t\t
\n\t\t\t\t\t

DEL SUGHERO MEDIANTE NANOINDENTAZIONE\n<\/h2>\t\t\t\t<\/div>\n\t\t\t\t<\/div>\n\t\t\t\t
\n\t\t\t\t
\n\t\t\t\t\t\t\t\t\t\t\t\t\t\t\t\"\"\t\t\t\t\t\t\t\t\t\t\t\t\t\t\t<\/div>\n\t\t\t\t<\/div>\n\t\t\t\t
\n\t\t\t\t
\n\t\t\t\t\t

Preparato da<\/h2>\t\t\t\t<\/div>\n\t\t\t\t<\/div>\n\t\t\t\t
\n\t\t\t\t
\n\t\t\t\t\t

FRANK LIU<\/h2>\t\t\t\t<\/div>\n\t\t\t\t<\/div>\n\t\t\t\t
\n\t\t\t\t
\n\t\t\t\t\t\t\t
\n\t\t\t
<\/div>\n\t\t<\/div>\n\t\t\t\t\t\t<\/div>\n\t\t\t\t<\/div>\n\t\t\t\t\t<\/div>\n\t\t<\/div>\n\t\t\t\t\t<\/div>\n\t\t<\/section>\n\t\t\t\t
\n\t\t\t\t\t\t
\n\t\t\t\t\t
\n\t\t\t
\n\t\t\t\t\t\t
\n\t\t\t\t
\n\t\t\t\t\t\t\t
\n\t\t\t
<\/div>\n\t\t<\/div>\n\t\t\t\t\t\t<\/div>\n\t\t\t\t<\/div>\n\t\t\t\t\t<\/div>\n\t\t<\/div>\n\t\t\t\t
\n\t\t\t
\n\t\t\t\t\t\t
\n\t\t\t\t
\n\t\t\t\t\t

INTRODUZIONE<\/h2>\t\t\t\t<\/div>\n\t\t\t\t<\/div>\n\t\t\t\t
\n\t\t\t\t
\n\t\t\t\t\t\t\t\t\t

L'analisi meccanica dinamica (DMA) \u00e8 una tecnica potente utilizzata per studiare le propriet\u00e0 meccaniche dei materiali. In questa applicazione, ci concentriamo sull'analisi del sughero, un materiale ampiamente utilizzato nei processi di sigillatura e invecchiamento del vino. Il sughero, ottenuto dalla corteccia della quercia Quercus suber, presenta strutture cellulari distinte che forniscono propriet\u00e0 meccaniche simili a quelle dei polimeri sintetici. In un asse, il sughero ha una struttura a nido d'ape. Gli altri due assi sono strutturati in prismi multipli di forma rettangolare. Ci\u00f2 conferisce al sughero propriet\u00e0 meccaniche diverse a seconda dell'orientamento testato.<\/p>\t\t\t\t\t\t\t\t<\/div>\n\t\t\t\t<\/div>\n\t\t\t\t

\n\t\t\t\t
\n\t\t\t\t\t

IMPORTANZA DELLE PROVE DI ANALISI MECCANICA DINAMICA (DMA) NELLA VALUTAZIONE DELLE PROPRIET\u00c0 MECCANICHE DEL SUGHERO<\/h2>\t\t\t\t<\/div>\n\t\t\t\t<\/div>\n\t\t\t\t
\n\t\t\t\t
\n\t\t\t\t\t\t\t\t\t

La qualit\u00e0 dei tappi di sughero dipende in larga misura dalle loro propriet\u00e0 meccaniche e fisiche, che sono fondamentali per la loro e\ufb00cacia nella sigillatura del vino. I fattori chiave che determinano la qualit\u00e0 del sughero includono la \ufb02essibilit\u00e0, l'isolamento, la resilienza e l'impermeabilit\u00e0 a gas e liquidi. Utilizzando test di analisi meccanica dinamica (DMA), possiamo valutare quantitativamente le propriet\u00e0 di \ufb02essibilit\u00e0 e resilienza dei tappi di sughero, fornendo un metodo di valutazione affidabile.<\/p>

Il tester meccanico NANOVEA PB1000 nel Nanoindentazione<\/a> consente di caratterizzare queste propriet\u00e0, in particolare il modulo di Young, il modulo di accumulo, il modulo di perdita e il tan delta (tan (\u03b4)). Il test DMA consente inoltre di raccogliere dati preziosi sullo sfasamento, la durezza, le sollecitazioni e le deformazioni del materiale di sughero. Grazie a queste analisi complete, \u00e8 possibile approfondire il comportamento meccanico dei tappi di sughero e la loro idoneit\u00e0 per le applicazioni di sigillatura del vino.<\/p>\t\t\t\t\t\t\t\t<\/div>\n\t\t\t\t<\/div>\n\t\t\t\t\t<\/div>\n\t\t<\/div>\n\t\t\t\t\t<\/div>\n\t\t<\/section>\n\t\t\t\t

\n\t\t\t\t\t\t
\n\t\t\t\t\t
\n\t\t\t
\n\t\t\t\t\t\t
\n\t\t\t\t
\n\t\t\t\t\t\t\t\t\t

OBIETTIVO DI MISURAZIONE<\/p>\t\t\t\t\t\t\t\t<\/div>\n\t\t\t\t<\/div>\n\t\t\t\t

\n\t\t\t\t\t\t
\n\t\t\t\t\t
\n\t\t\t
\n\t\t\t\t\t\t
\n\t\t\t\t
\n\t\t\t\t\t\t\t\t\t

In questo studio, \u00e8 stata eseguita un'analisi meccanica dinamica (DMA) su quattro tappi di sughero utilizzando il tester meccanico NANOVEA PB1000 in modalit\u00e0 di nanoindentazione. La qualit\u00e0 dei tappi di sughero \u00e8 etichettata come: 1 - Flor, 2 - First, 3 - Colmato, 4 - Gomma sintetica. Le prove di indentazione DMA sono state condotte sia in direzione assiale che radiale per ciascun tappo di sughero. Analizzando la risposta meccanica dei tappi di sughero, abbiamo cercato di capire il loro comportamento dinamico e di valutare le loro prestazioni in caso di orientamenti diversi.<\/p>\t\t\t\t\t\t\t\t<\/div>\n\t\t\t\t<\/div>\n\t\t\t\t

\n\t\t\t\t
\n\t\t\t\t\t\t\t\t\t

NANOVEA<\/p>\t\t\t\t\t\t\t\t<\/div>\n\t\t\t\t<\/div>\n\t\t\t\t

\n\t\t\t\t
\n\t\t\t\t\t\t\t\t\t

PB1000<\/p>\t\t\t\t\t\t\t\t<\/div>\n\t\t\t\t<\/div>\n\t\t\t\t

\n\t\t\t\t
\n\t\t\t\t\t\t\t\t\t
\n\t\t\t\t\t\n\t\t\t\t\t\t\n\t\t\t\t\t\t\t\t\tSAPERNE DI PI\u00d9<\/span>\n\t\t\t\t\t<\/span>\n\t\t\t\t\t<\/a>\n\t\t\t\t<\/div>\n\t\t\t\t\t\t\t\t<\/div>\n\t\t\t\t<\/div>\n\t\t\t\t\t<\/div>\n\t\t<\/div>\n\t\t\t\t
\n\t\t\t
\n\t\t\t\t\t\t
\n\t\t\t\t
\n\t\t\t\t\t\t\t\t\t\t\t\t\t\t\t\t\n\t\t\t\t\t\t\t\"\"\t\t\t\t\t\t\t\t<\/a>\n\t\t\t\t\t\t\t\t\t\t\t\t\t\t\t<\/div>\n\t\t\t\t<\/div>\n\t\t\t\t\t<\/div>\n\t\t<\/div>\n\t\t\t\t\t<\/div>\n\t\t<\/section>\n\t\t\t\t\t<\/div>\n\t\t<\/div>\n\t\t\t\t\t<\/div>\n\t\t<\/section>\n\t\t\t\t
\n\t\t\t\t\t\t
\n\t\t\t\t\t
\n\t\t\t
\n\t\t\t\t\t\t
\n\t\t\t\t
\n\t\t\t\t\t

PARAMETRI DEL TEST<\/h2>\t\t\t\t<\/div>\n\t\t\t\t<\/div>\n\t\t\t\t
\n\t\t\t\t
\n\t\t\t\t\t\t\t\t\t
FORZA MASSIMA<\/strong><\/em><\/td>75 mN<\/strong><\/em><\/td><\/tr>
TASSO DI CARICO<\/strong><\/em><\/td>150 mN\/min<\/strong><\/em><\/td><\/tr>
TASSO DI SCARICO<\/strong><\/em><\/td>150 mN\/min<\/strong><\/em><\/td><\/tr>
AMPLITUDINE<\/strong><\/em><\/td>5 mN<\/strong><\/em><\/td><\/tr>
FREQUENZA<\/strong><\/em><\/td>1 Hz<\/strong><\/em><\/td><\/tr>
CREEP<\/strong><\/em><\/td>60 s<\/strong><\/em><\/td><\/tr><\/tbody><\/table>\t\t\t\t\t\t\t\t<\/div>\n\t\t\t\t<\/div>\n\t\t\t\t
\n\t\t\t\t\t\t
\n\t\t\t\t\t
\n\t\t\t
\n\t\t\t\t\t\t
\n\t\t\t\t
\n\t\t\t\t\t\t\t\t\t

tipo di penetratore<\/span><\/p>

Palla<\/span><\/p>

51200 Acciaio<\/span><\/p>

Diametro 3 mm<\/span><\/p>\t\t\t\t\t\t\t\t<\/div>\n\t\t\t\t<\/div>\n\t\t\t\t\t<\/div>\n\t\t<\/div>\n\t\t\t\t

\n\t\t\t
\n\t\t\t\t\t\t
\n\t\t\t\t
\n\t\t\t\t\t\t\t\t\t\t\t\t\t\t\t\"\"\t\t\t\t\t\t\t\t\t\t\t\t\t\t\t<\/div>\n\t\t\t\t<\/div>\n\t\t\t\t\t<\/div>\n\t\t<\/div>\n\t\t\t\t\t<\/div>\n\t\t<\/section>\n\t\t\t\t\t<\/div>\n\t\t<\/div>\n\t\t\t\t\t<\/div>\n\t\t<\/section>\n\t\t\t\t
\n\t\t\t\t\t\t
\n\t\t\t\t\t
\n\t\t\t
\n\t\t\t\t\t\t
\n\t\t\t\t
\n\t\t\t\t\t

RISULTATI<\/h2>\t\t\t\t<\/div>\n\t\t\t\t<\/div>\n\t\t\t\t
\n\t\t\t\t
\n\t\t\t\t\t\t\t\t\t

Nelle tabelle e nei grafici seguenti vengono confrontati il modulo di Young, il modulo di accumulo, il modulo di perdita e il tan delta tra ciascun campione e orientamento.<\/p>

Modulo di Young: <\/i><\/b>Sti\ufb00ness; valori elevati indicano sti\ufb00, valori bassi indicano \ufb02essibilit\u00e0.<\/p>

Modulo di stoccaggio: <\/i><\/b>Risposta elastica; energia immagazzinata nel materiale.<\/p>

Modulo di perdita: <\/i><\/b>Risposta viscosa; energia persa a causa del calore.<\/p>

Abbronzatura (\u03b4): <\/i><\/b>Smorzamento; valori elevati indicano un maggiore smorzamento.<\/p>

ORIENTAMENTO ASSIALE<\/strong><\/em><\/p>
Tappo<\/i><\/b><\/td>MODULO DI YOUNG<\/i><\/b><\/td>MODULO DI ACCUMULO<\/i><\/b><\/td>MODULO DI PERDITA<\/i><\/b><\/td>TAN<\/i><\/b><\/td><\/tr>
#<\/i><\/b><\/td>(MPa)<\/i><\/b><\/td>(MPa)<\/i><\/b><\/td>(MPa)<\/i><\/b><\/td>(\u03b4)<\/i><\/b><\/td><\/tr>
1<\/td>22.5675<\/td>22.27209<\/td>3.624947<\/td>0.162964<\/td><\/tr>
2<\/td>18.54664<\/td>18.27153<\/td>3.162349<\/td>0.17409<\/td><\/tr>
3<\/td>23.75381<\/td>23.47267<\/td>3.617819<\/td>0.154592<\/td><\/tr>
4<\/td>23.6972<\/td>23.58064<\/td>2.347008<\/td>0.099539<\/td><\/tr><\/tbody><\/table>



ORIENTAMENTO RADIALE<\/strong><\/em><\/p>
Tappo<\/i><\/b><\/td>MODULO DI YOUNG<\/i><\/b><\/td>MODULO DI ACCUMULO<\/i><\/b><\/td>MODULO DI PERDITA<\/i><\/b><\/td>TAN<\/i><\/b><\/td><\/tr>
#<\/i><\/b><\/td>(MPa)<\/i><\/b><\/td>(MPa)<\/i><\/b><\/td>(MPa)<\/i><\/b><\/td>(\u03b4)<\/i><\/b><\/td><\/tr>
1<\/td>24.78863<\/td>24.56542<\/td>3.308224<\/td>0.134865<\/td><\/tr>
2<\/td>26.66614<\/td>26.31739<\/td>4.286216<\/td>0.163006<\/td><\/tr>
3<\/td>44.07867<\/td>43.61426<\/td>6.365979<\/td>0.146033<\/td><\/tr>
4<\/td>28.04751<\/td>27.94148<\/td>2.435978<\/td>0.087173<\/td><\/tr><\/tbody><\/table>\t\t\t\t\t\t\t\t<\/div>\n\t\t\t\t<\/div>\n\t\t\t\t\t<\/div>\n\t\t<\/div>\n\t\t\t\t\t<\/div>\n\t\t<\/section>\n\t\t\t\t
\n\t\t\t\t\t\t
\n\t\t\t\t\t
\n\t\t\t
\n\t\t\t\t\t\t
\n\t\t\t\t\t\t
\n\t\t\t\t\t
\n\t\t\t
\n\t\t\t\t\t\t
\n\t\t\t\t
\n\t\t\t\t\t\t\t\t\t

MODULO DI YOUNG<\/p>\t\t\t\t\t\t\t\t<\/div>\n\t\t\t\t<\/div>\n\t\t\t\t

\n\t\t\t\t
\n\t\t\t\t\t\t\t\t\t\t\t\t\t\t\t\"\"\t\t\t\t\t\t\t\t\t\t\t\t\t\t\t<\/div>\n\t\t\t\t<\/div>\n\t\t\t\t\t<\/div>\n\t\t<\/div>\n\t\t\t\t
\n\t\t\t
\n\t\t\t\t\t\t
\n\t\t\t\t
\n\t\t\t\t\t\t\t\t\t

MODULO DI ACCUMULO<\/p>\t\t\t\t\t\t\t\t<\/div>\n\t\t\t\t<\/div>\n\t\t\t\t

\n\t\t\t\t
\n\t\t\t\t\t\t\t\t\t\t\t\t\t\t\t\"\"\t\t\t\t\t\t\t\t\t\t\t\t\t\t\t<\/div>\n\t\t\t\t<\/div>\n\t\t\t\t\t<\/div>\n\t\t<\/div>\n\t\t\t\t\t<\/div>\n\t\t<\/section>\n\t\t\t\t
\n\t\t\t\t\t\t
\n\t\t\t\t\t
\n\t\t\t
\n\t\t\t\t\t\t
\n\t\t\t\t
\n\t\t\t\t\t\t\t\t\t

MODULO DI PERDITA<\/p>\t\t\t\t\t\t\t\t<\/div>\n\t\t\t\t<\/div>\n\t\t\t\t

\n\t\t\t\t
\n\t\t\t\t\t\t\t\t\t\t\t\t\t\t\t\"\"\t\t\t\t\t\t\t\t\t\t\t\t\t\t\t<\/div>\n\t\t\t\t<\/div>\n\t\t\t\t\t<\/div>\n\t\t<\/div>\n\t\t\t\t
\n\t\t\t
\n\t\t\t\t\t\t
\n\t\t\t\t
\n\t\t\t\t\t\t\t\t\t

TAN DELTA<\/p>\t\t\t\t\t\t\t\t<\/div>\n\t\t\t\t<\/div>\n\t\t\t\t

\n\t\t\t\t
\n\t\t\t\t\t\t\t\t\t\t\t\t\t\t\t\"\"\t\t\t\t\t\t\t\t\t\t\t\t\t\t\t<\/div>\n\t\t\t\t<\/div>\n\t\t\t\t\t<\/div>\n\t\t<\/div>\n\t\t\t\t\t<\/div>\n\t\t<\/section>\n\t\t\t\t
\n\t\t\t\t
\n\t\t\t\t\t\t\t\t\t

Tra i tappi di sughero, il modulo di Young non \u00e8 molto diverso quando viene testato in direzione assiale. Solo i tappi #2 e #3 mostrano un'apparente differenza nel modulo di Young tra la direzione radiale e quella assiale. Di conseguenza, anche il modulo di accumulo e il modulo di perdita saranno pi\u00f9 alti in direzione radiale che in direzione assiale. Il tappo #4 presenta caratteristiche simili a quelle dei tappi in sughero naturale, tranne che per il modulo di perdita. Questo dato \u00e8 molto interessante perch\u00e9 significa che il sughero naturale ha una propriet\u00e0 pi\u00f9 viscosa rispetto al materiale in gomma sintetica.<\/p>\t\t\t\t\t\t\t\t<\/div>\n\t\t\t\t<\/div>\n\t\t\t\t\t<\/div>\n\t\t<\/div>\n\t\t\t\t\t<\/div>\n\t\t<\/section>\n\t\t\t\t

\n\t\t\t\t\t\t
\n\t\t\t\t\t
\n\t\t\t
\n\t\t\t\t\t\t
\n\t\t\t\t
\n\t\t\t\t\t

CONCLUSIONE<\/h2>\t\t\t\t<\/div>\n\t\t\t\t<\/div>\n\t\t\t\t
\n\t\t\t\t\t\t
\n\t\t\t\t\t
\n\t\t\t
\n\t\t\t\t\t\t\t<\/div>\n\t\t<\/div>\n\t\t\t\t
\n\t\t\t
\n\t\t\t\t\t\t
\n\t\t\t\t
\n\t\t\t\t\t\t\t
\n\t\t\t
<\/div>\n\t\t<\/div>\n\t\t\t\t\t\t<\/div>\n\t\t\t\t<\/div>\n\t\t\t\t
\n\t\t\t\t
\n\t\t\t\t\t\t\t\t\t

La NANOVEA Collaudatore meccanico<\/a> nella modalit\u00e0 Nano Scratch Tester consente la simulazione di molti guasti reali dei rivestimenti di vernice e dei rivestimenti duri. Applicando carichi crescenti in modo controllato e attentamente monitorato, lo strumento permette di individuare in quali momenti si verificano cedimenti di carico. Questo pu\u00f2 quindi essere utilizzato come metodo per determinare valori quantitativi per la resistenza ai graffi. \u00c8 noto che il rivestimento testato, senza agenti atmosferici, presenta una prima fessura a circa 22 mN. Con valori pi\u00f9 vicini a 5 mN, \u00e8 chiaro che il giro di 7 anni ha degradato la vernice.<\/p>\n

La compensazione del profilo originale consente di ottenere una profondit\u00e0 corretta durante il graffio e di misurare la profondit\u00e0 residua dopo il graffio. Ci\u00f2 fornisce ulteriori informazioni sul comportamento plastico ed elastico del rivestimento in presenza di un carico crescente. Sia la fessurazione che le informazioni sulla deformazione possono essere di grande utilit\u00e0 per migliorare il rivestimento duro. Le deviazioni standard molto ridotte dimostrano anche la riproducibilit\u00e0 della tecnica dello strumento, che pu\u00f2 aiutare i produttori a migliorare la qualit\u00e0 del loro rivestimento\/vernice dura e a studiare gli effetti degli agenti atmosferici.<\/p>\t\t\t\t\t\t\t\t<\/div>\n\t\t\t\t<\/div>\n\t\t\t\t

\n\t\t\t\t
\n\t\t\t\t\t\t\t
\n\t\t\t
<\/div>\n\t\t<\/div>\n\t\t\t\t\t\t<\/div>\n\t\t\t\t<\/div>\n\t\t\t\t\t<\/div>\n\t\t<\/div>\n\t\t\t\t\t<\/div>\n\t\t<\/section>\n\t\t\t\t\t<\/div>\n\t\t<\/div>\n\t\t\t\t\t<\/div>\n\t\t<\/section>\n\t\t\t\t
\n\t\t\t\t\t\t
\n\t\t\t\t\t
\n\t\t\t
\n\t\t\t\t\t\t
\n\t\t\t\t
\n\t\t\t\t\t

Avete un'applicazione simile?<\/h2>\t\t\t\t<\/div>\n\t\t\t\t<\/div>\n\t\t\t\t
\n\t\t\t\t
\n\t\t\t\t\t\t\t\t\t
\n\t\t\t\t\t\n\t\t\t\t\t\t\n\t\t\t\t\t\t\t\t\tDISCUTETE SUBITO CON UN ESPERTO<\/span>\n\t\t\t\t\t<\/span>\n\t\t\t\t\t<\/a>\n\t\t\t\t<\/div>\n\t\t\t\t\t\t\t\t<\/div>\n\t\t\t\t<\/div>\n\t\t\t\t
\n\t\t\t\t
\n\t\t\t\t\t\t\t\t\t
\n\t\t\t\t\t\n\t\t\t\t\t\t\n\t\t\t\t\t\t\t\t\tOTTENERE RAPIDAMENTE PREZZI E DETTAGLI<\/span>\n\t\t\t\t\t<\/span>\n\t\t\t\t\t<\/a>\n\t\t\t\t<\/div>\n\t\t\t\t\t\t\t\t<\/div>\n\t\t\t\t<\/div>\n\t\t\t\t\t<\/div>\n\t\t<\/div>\n\t\t\t\t\t<\/div>\n\t\t<\/section>\n\t\t\t\t<\/div>","protected":false},"excerpt":{"rendered":"

DYNAMIC MECHANICAL ANALYSIS OF CORK USING NANOINDENTATION Prepared by FRANK LIU INTRODUCTION Dynamic Mechanical Analysis (DMA) is a powerful technique used to investigate the mechanical properties of materials. In this application, we focus on the analysis of cork, a widely used material in wine sealing and aging processes. Cork, obtained from the bark of the […]<\/p>","protected":false},"author":1,"featured_media":22112,"comment_status":"open","ping_status":"open","sticky":false,"template":"","format":"standard","meta":{"_exactmetrics_skip_tracking":false,"_exactmetrics_sitenote_active":false,"_exactmetrics_sitenote_note":"","_exactmetrics_sitenote_category":0,"footnotes":""},"categories":[7,338,343,349,337],"tags":[],"class_list":["post-22101","post","type-post","status-publish","format-standard","has-post-thumbnail","hentry","category-application-notes","category-indentation-hardness-elastic","category-loss-storage","category-laboratory-testing","category-mechanical-testing"],"_links":{"self":[{"href":"https:\/\/nanovea.com\/it\/wp-json\/wp\/v2\/posts\/22101","targetHints":{"allow":["GET"]}}],"collection":[{"href":"https:\/\/nanovea.com\/it\/wp-json\/wp\/v2\/posts"}],"about":[{"href":"https:\/\/nanovea.com\/it\/wp-json\/wp\/v2\/types\/post"}],"author":[{"embeddable":true,"href":"https:\/\/nanovea.com\/it\/wp-json\/wp\/v2\/users\/1"}],"replies":[{"embeddable":true,"href":"https:\/\/nanovea.com\/it\/wp-json\/wp\/v2\/comments?post=22101"}],"version-history":[{"count":21,"href":"https:\/\/nanovea.com\/it\/wp-json\/wp\/v2\/posts\/22101\/revisions"}],"predecessor-version":[{"id":24684,"href":"https:\/\/nanovea.com\/it\/wp-json\/wp\/v2\/posts\/22101\/revisions\/24684"}],"wp:featuredmedia":[{"embeddable":true,"href":"https:\/\/nanovea.com\/it\/wp-json\/wp\/v2\/media\/22112"}],"wp:attachment":[{"href":"https:\/\/nanovea.com\/it\/wp-json\/wp\/v2\/media?parent=22101"}],"wp:term":[{"taxonomy":"category","embeddable":true,"href":"https:\/\/nanovea.com\/it\/wp-json\/wp\/v2\/categories?post=22101"},{"taxonomy":"post_tag","embeddable":true,"href":"https:\/\/nanovea.com\/it\/wp-json\/wp\/v2\/tags?post=22101"}],"curies":[{"name":"wp","href":"https:\/\/api.w.org\/{rel}","templated":true}]}}